RESUMO
The development of functional materials from food waste sources and minerals is currently of high importance. In the present work, polylactic acid (PLA)/silica composites were prepared by in situ ring-opening polymerizations of L-lactide onto the surface of pristine (Silochrom) and amine-functionalized (Silochrom-NH2) silica. The characteristics of the ring-opening polymerization onto the surface of modified and unmodified silica were identified and discussed. Fourier transform infrared spectroscopy was used to confirm the polymerization of lactide onto the silica surface, and thermogravimetric analysis determined that PLA constituted 5.9% and 7.5% of the composite mass for Silochrom/PLA and Silochrom-NH2/PLA, respectively. The sorption properties of the composites with respect to Pb(II), Co(II), and Cu(II) ions were investigated, and the effect of contact time, initial metal ion concentration, and initial pH were evaluated. Silochrom-NH2/PLA composites were found to have a higher adsorption capacity than Silochrom/PLA for all chosen ions, with the highest adsorption value occurring for Pb2+ at 1.5 mmol/g (90% removal efficiency). The composites showed the highest performance in the neutral or near-neutral pH (created by distilled water or buffer pH 6.86) during the first 15 min of phase contact. The equilibrium characteristics of adsorption were found to follow the Langmuir isotherm model rather than the Freundlich and Temkin models. Perspective applications for these PLA/silicas include remediation of industrial wastewater or leaching solutions from spent lead-acid and Li-ion batteries.
RESUMO
SUMMARY: Regeneration of the dura mater following duraplasty using a collagen film, a chitosan film, or a combination of both with gelatin, was studied in a craniotomy and penetrating brain injury model in rats. Collagen autofluorescence in the regenerated dura mater was evaluated using confocal microscopy with excitation at λem = 488 nm and λem = 543 nm. An increase in regeneration of the extracellular matrix of connective tissue and an increase in matrix fluorescence were detected at 6 weeks after duraplasty. The major contributors to dura mater regeneration were collagen films, chitosan plus gelatin-based films, and, to a much lesser extent, chitosan-based films. By using autofluorescence densitometry of extracellular matrix, the authors were able to quantify the degree of connective tissue regeneration in the dura mater following duraplasty.
RESUMEN: Se estudió la regeneración de la duramadre después de una duraplastía utilizando una lámina de colágeno, una lamina de quitosano o una combinación de ambas con gelatina en un modelo de craneotomía y lesión cerebral en ratas. La autofluorescencia del colágeno en la duramadre regenerada se evaluó mediante microscopía confocal con excitación a λem = 488 nm y λem = 543 nm. Se observó un aumento en la regeneración de la matriz extracelular del tejido conectivo y un aumento en la fluorescencia de la matriz a las 6 semanas después de la duraplastía. Se observe un efecto significativo en la regeneración de la duramadre con las láminas de colágeno, las láminas en base de quitosano más gelatina y, en un menor grado, las láminas a base de quitosano. Mediante el uso de densitometría de autofluorescencia de la matriz extracelular, los autores lograron cuantificar el grado de regenera- ción del tejido conectivo en la duramadre después de la duraplastía.